Original Article

AVALIAÇÃO DA GRANULOMETRIA DE PARTÍCULAS DE Pinus taeda COMBINADAS COM ADESIVOS COMERCIAIS PARA A FABRICAÇÃO DE AGLOMERADOS

PINUS TAEDA PARTICLE SIZE VALUATION MIXED WITH COMMERCIAL RESIN TO PARTICLEBOARDS MANUFACTURE

Peixoto, Gustavo Luna; Brito, Edvá Oliveira

Downloads: 0
Views: 1203

Resumo

Nesse trabalho avaliou-se a granulometria de partículas de madeira de Pinus taeda em combinação com adesivos comerciais para a fabricação de chapas de madeira aglomerada. Foram produzidas chapas utilizando duas granulometrias – partículas que passaram em peneira com malha de 4,37 mm de diâmetro e ficaram retidas em peneira de 0,61 mm (tipo A); e partículas que passaram em peneira de 2,00 mm de diâmetro e ficaram retidas em peneira de 0,61 mm de diâmetro (tipo B). O conteúdo de adesivo utilizado foi de 8% (base peso seco) tanto para Uréia formaldeído (PL 2080) como para fenol formaldeído (PB 2045). Avaliou-se as propriedades de flexão estática, ligação interna e inchamento em espessura (norma americana ASTM D-1037). As chapas produzidas com partículas de granulometria menor (tipo B) apresentaram maior resitência à tração, enquanto que aquelas produzidas com partículas de maior granulometria (tipo A) apresentaram maior resistência à flexão estática. As chapas produzidas com adesivo fenol formaldeído foram mais resistentes à flexão estática. Em relação ao inchamento em espessura, as chapas feitas a partir de adesivos fenol formaldeído e particulas do tipo A, apresentaram menores valores. Pode-se concluir finalmente que partículas, como as utilizadas neste trabalho, geralmente produzidas a partir de resíduos de madeira, podem gerar chapas com qualidade satisfatória.

Palavras-chave

Pinus taeda, granulometria de partículas, adesivos, chapas de partículas

Abstract

In this work was evaluated the Pinus taeda particle size mixed with commercial resin to particleboard manufacture. Particleboards were made from two size particles (particles that went through a screen with mesh of 4,37mm in size and was hold in a screen with mesh of 0,61 mm in size (particle A); and particles that went through a screen with mesh of 2,00 mm in size and was hold in a screen with mesh of 0,61 mm in size (particle B)). The resin content was 8% (dry weight base) to urea- formaldehyde and phenol formaldehyde. The evaluated properties were static bending, internal bond and thickness swelling, by ASTM D-1037 standard. Particleboards made from small size particles (particle B) showed bigger internal bond, while particleboards made from bigger size particles (particle A) showed increasing static bending. Particleboards made from phenol-formaldehyde resin showed better properties of static bending. Better results in thickness swelling was obtained by particleboards made from phenol-formaldehyde resin and particles A.

Keywords

Pinus taeda, particle size, resin, particleboard