Original Article Wood Science and Technology

Technological Feasibility of Hovenia dulcis thunb. Species for the Production of Edge Glued Panels

Raquel Marchesan; Pedro Lício Loiola; Tânia Vieira de Mello; Márcio Pereira da Rocha; José Reinaldo Moreira da Silva

Abstract

ABSTRACT: This study aims to evaluate the use of Hovenia dulcis wood to produce Edge Glued Panels – EGP. To this end, joints with dimensions of 5.0 × 31.0 × 2.5 cm (Width × Length × Thickness) were put together using polyvinyl acetate (PVAc) and emulsion polymer isocyanate (EPI) adhesives at a spread rate of 200 g.m-2 and the chemical characterization of the wood was performed. The strength of glued joints was evaluated through shear tests based on the procedures described by established standards. The results showed that the EPI adhesive achieved the best results in edge gluing to produce EGP. The use of PVAc adhesive did not show satisfactory results for edge gluing under these conditions. Hovenia dulcis wood is indicated for producing higher value-added wood products - (VAWP) for external use purposes.

Keywords

uva-do-japao, value added wood products, gluing

References

Albino VCS, Mori FA, Mendes LM. Influência das características anatômicas e do teor de extrativos totais da madeira de Eucalyptus grandis w. Hill ex Maiden na qualidade da colagem. Ciência Florestal 2012; 22(4): 803-811. http://dx.doi.org/10.5902/198050987561.

Almeida VC. Avaliação do potencial de uso de resíduos de madeira tropical para produção de painel colado lateralmente - EGP [tese]. Curitiba: Universidade Federal do Paraná; 2013.

American Society for Testing Materials – ASTM. ASTM 5572-95: standard specification for adhesives used for finger joints in nonstructural lumber products. West Conshohocken: ASTM; 1999. 17 p.

Bednarczuk E. Produção de lâminas e painel compensado multilaminado com madeira de Hovenia dulcis Thunberg (uva-do-japão) [dissertação]. Irati: Universidade Estadual do Centro-Oeste; 2015.

Bianche J. J. Interface madeira-adesivo e resistência de juntas coladas com diferentes adesivos e gramatura [tese]. Viçosa: Universidade Federal de Viçosa; 2014.

Bila NF. Avaliação da qualidade de juntas coladas de seis espécies de madeiras tropicais da Amazônia [dissertação]. Curitiba: Universidade Federal do Paraná; 2014.

Carvalho A. Denominações convencionais para propriedades da madeira. In: Carvalho A. Tecnologia das indústrias da madeira III – Na2 . Lisboa: Direcção Geral das Florestas; 1996. 5 p. vol. I.

Carvalho PER. Ecologia, silvicultura e usos da uva-do-japão (Hovenia dulcis Thunberg). Colombo: EMBRAPA-CNPF; 1994. 24 p. (Circular Técnica; no. 23).

European Standard – EN. EN 1245: adhesives: determination of ph: test method . Bruxelas: EN; 2001a.

European Standard – EN. EN 12092: adhesives: determination of viscosity: test method . Bruxelas: EN; 2001b.

European Standard – EN. EN 13353: solid wood panels (SWP): requirements . Bruxelas: EN; 2008.

European Standard – EN. EN 13354: solid wood panels (SWP): bonding quality . Bruxelas: EN; 2009.

European Standard – EN. EN 827: Adhesives – Determination of convencional solids content and constant mass solids content- Test Method . Bruxelas: EN; 2005.

Haubrich JL, Gonçalves C, Tonet A. Adesivos vinílicos apresentam soluções para madeira. Revista da Madeira 2007; 103: 66-70.

Indústria Brasileira de Árvores – IBÁ. Anuário estatístico da IBÁ 2014: ano base 2013. Brasília: IBÁ; 2014. 100 p.

Instituto Brasileiro do Meio Ambiente e dos Recursos Naturais Renováveis – IBAMA. Banco de dados de madeiras brasileiras. Brasília: IBAMA; 2014. [cited 2014 Nov 13]. Available from: http://www.ibama.gov.br

Iwakiri S, Trianoski R, Cunha AB, Prata JG, Hara M, Bila NF et al. Avaliação da resistência de juntas coladas da madeira de Eucalyptus benthamii com diferentes adesivos e faces de colagem. Scientia Forestalis 2013; 41(99)

Iwakiri S. Painéis de madeira reconstituída. Curitiba: FUPEF; 2005.

Jankowsky IP. Colagem de madeiras. Piracicaba: Escola Superior de Agricultura “Luiz de Queiroz”; 1988. 45 p.

Klock U, Muñiz GIB, Hernandez JA, Andrade AS. Química da madeira . 3. ed. Curitiba: Universidade Federal do Paraná; 2005. 86 p. Apostila.

Kollmann FEP, Côte WA Jr. Principles of wood science and technology . New York: Springer-Verlarg; 1968. 592 p. http://dx.doi.org/10.1007/978-3-642-87928-9.

Lima CKP, Mori FA, Mendes LM, Carneiro ACO. Características anatômicas e química da madeira de clones de Eucalyptus e sua influência na colagem. Cerne 2007; 13(2): 123-129.

Loiola PL. Secagem da madeira de teca (Tectona grandis L. f) sob diferentes condições [dissertação]. Curitiba: Universidade Federal do Paraná; 2015.

Marcati CR, Della Lucia RM. Comportamento do angicovermelho (Piptadenia peregrinabenth.) à adesão com PVA (acetato de polivinila) e resorcinol formaldeído. Revista Ceres 1996; 2(1): 7.

Marra AA. Tecnology of wood bonding: principles in practice. New York: Van Nostrand Renhold; 1992. 453 p.

Mattos RLG, Gonçalves RM, Chagas FB. Painéis de madeira no Brasil: panorama e perspectivas. BNDES Setorial 2008; 27: 121-156.

Miranda ROV, Rancatti H, Machado GO, Soares ID, Roik M. Caracterização química e potencial de utilização da madeira de Hovenia dulcis Thunb. Enciclopédia Biosfera 2013; 9: 627-635.

Motta JP, Oliveira JTS, Braz RL, Duarte APC, Alves RC. Caracterização da madeira de quatro espécies florestais. Ciência Rural 2014; 44(12): 2186-2192. http://dx.doi.org/10.1590/0103-8478cr20130479.

Plaster OB, Oliveira JTS, Gonçalves FG, Motta JP. Comportamento de adesão da madeira de um híbrido clonal de Eucalyptus urophylla x Eucalyptus grandis proveniente de três condições de manejo. Ciência Florestal 2012; 22(2): 323-330. http://dx.doi.org/10.5902/198050985739.

Prata JG. Estudo da viabilidade tecnológica do uso de espécies de pinus tropicais para produção de painéis colados lateralmente (Edge Glued Panels – EGP) [tese]. Curitiba: Universidade Federal do Paraná; 2010.

Rigatto PA, Pereira JCD, Mattos PP, Schaitza EG. Características físicas, químicas e anatômicas da madeira de Hovenia dulcis. Colombo: Ministério da Cultura e do Meio Ambiente; 2001. (Comunicado Técnico; no. 66).

Sellers T Jr. Adhesive in the wood industry. In: Pizzi A, Mittal KL, editor. Handbook of adhesive technology. New York: Marcel Dekker; 1994. p. 599-614. cap. 37.

Technical Association of The Pulp and Paper Industry – TAPPI. TAPPI T-264 om-07: preparation of wood for chemical analysis. Atlanta: TAPPI Press; 1997a.

Technical Association of The Pulp and Paper Industry – TAPPI. TAPPI T-204 cm-97: solvent extractives of wood and pulp. Atlanta: TAPPI Press; 1997b.

Technical Association of The Pulp and Paper Industry – TAPPI. TAPPI T-252 Om-12: pH and Electrical Conductivity of Hot Water Extracts of Pulp, Paper and Paperboard . Atlanta: TAPPI Press; 2002a.

Technical Association of The Pulp and Paper Industry – TAPPI. TAPPI TAPPI T-222 om-15: acid: insoluble lignin in wood and pulp. Atlanta: TAPPI Press, 2002b.

Technical Association of The Pulp and Paper Industry – TAPPI. TAPPI T-211 om-12: ash in wood, pulp, paper and paperboard: combustion at 525 °C. Atlanta: TAPPI Press; 2002c.

Vivian MA, Modes KS, Beltrame R, Souza JT, Stangerlin DM, Morais WWC et al. Influência do tratamento térmico nos defeitos de secagem da madeira de Hovenia dulcis Thunb. Ciência da Madeira 2011; 2(1): 15-38. http://dx.doi.org/10.12953/2177-6830.v02n01a02.
 

5ac36fa60e88253d39de5141 floram Articles
Links & Downloads

FLORAM

Share this page
Page Sections